1.2344, H13 Hot

Basic Info.

Model NO.	1.2344, H13
Special Use	Mold Steel
Delivery Condition	Annealed, Quenched+Tempered
Quality Standard	BS En ISO 4957
Surface Condition	Black, Grinded, Peeled, Rough Turned, Polished
Steel-Making Condition	Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+ESR
Size Range	10-820mm
Transport Package	Sea Worth Packaging
Specification	1.2344, H13
Trademark	Chengquan
Origin	Huangshi, China
HS Code	7228600000
Production Capacity	500tons Per Month

Product Description

Similar Grade: 1.2344, H13.
Shape: Round, Flat, Square.
Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	50-420	-	-	2000-5800
Square	50-420	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed, Quenched+Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1. Competitive price
2. Immediate delivery
3. Premium quality
4. Reliable service

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

Chemical Composition:

Grade	C	Mn	P	S	Si	Cr	V	Mo
1.2344	0.32-0.45	0.20-0.60	0.030 max	0.030 max	0.80-1.25	4.75-5.5	0.80-1.2	1.10-1.75

Mechanical Property:
UT: Material will be ultrasonically tested at appropriate stages of the manufacture to ensure the quality, as agreed between seller and purchaser.
Heat Treatment:
Hardness :Annealed(+A) max: 235 BHN
1.2344 tool steel when heat-treatment the preheat Temperature need reach 788°C, and the temperature may be ± 14 °C .
1.2344 tool steel when austenitizing ,should keep 5-15 minutes long. If is the salt bath ,temperature should keep in the 996 °C,and shall be ± 5.6 °C. Or is the controlled atmosphere furnaces,temperature should keep in the 1010 °C,and shall be ± 5.6 °C.
Quenching: 1.2344 tool steel Hardening quenching using air cooling, and it's hardness min is 52 RC.
Tempering: 1.2344 tool steel general tempering temperature is 552°C. Double tempering of Double tempering of H13 tool steel is recommended.
Application:
1.2344 tool steel are frequently used in cold work applications requiring toughness at relatively high hardness
For high-speed forging die. Aluminum, magnesium alloy forging die, hardness select 42-50HRC. Ferrous metal die, hardness select 40-50HRC. Suitable for the application of cracks greater risk of hot die steel, tool steel life of the mold can be 1.5-3 times 5CrNiMo steel
Description:
1.2344 tool steel is characterized by a controlled chromium content along with other alloying elements.
1.2344 tool steel with excellent toughness
1.2344 tool steel with high hardenability

1.2344, H13 Hot-Work Tool Steel with Best Quality